Hot Rolling Steel

Hot Extruding Steel

Cold Drawing Steel

Cold Drawn Steel - Hot Rolled Steel - Steel Extrusions - Cold Rolled Steel - Specially Engineered Milled Steel

Consult with us today at 313-570-5712 to discuss how our steel manufacturing process for Cold Drawn Steel - Cold Drawing, Hot Rolled Steel Shapes – Hot Rolling, Hot extruding – Extruded Steel Shapes – Steel Extrusions, and Cold Rolling – Cold Forming – Roll Forming Steel Shapes can be a cost effective solution when compared to machining, welding, forging, casting, powder metal and other steel forming processes including our Specially Engineered Milled (SE-|M|®)process for Tight Tolerance and  Optimum Hardness.

 

Cold Drawn Steel - Cold Drawing

Cold Drawn Steel – Cold Drawing

Cold Drawn Steel. The process of cold drawing is a procedure by which steel profiles are formed in order to achieve complex cross sections of excellent precision in these cold drawn steel shapes. After careful pre-treatment and de-scaling, the special profile bars are drawn through a forming die. This operation can be repeated up to three or four times.

Cold drawing of hot rolled and hot extruded special pre-shape steel profiles tightens the cross-sectional tolerances, thus leading to significant improvement in dimensional accuracy and surface quality. Cold drawn steel special profiles offer the same precision achieved by machining but without the waste.

Cold drawn special profiles offer extensive advantages, among other things:

  • Smooth and scale-free surface
  • Sharp edges
  • Uninterrupted grain orientation
  • Increased tensile strength and yield point

Applications include many cold drawn steel shapes such as both carbon and stainless steel fittings, various stainless steel shapes used in aerospace applications, linear motion and machinery applications.
The economical advantages of using cold drawn stainless steel profiles are so numerous that in most cases stainless steel profiles offer the best solution to custom engineered designs.


Hot Rolled Steel - Hot Rolling

Hot Rolled Steel Shapes – Hot Rolling

During the production of special hot rolled steel profiles by hot rolling the input billet or slab is formed into lengths up to 70 m using two oppositely rotating cylindrical rolls. The hot rolled steel shapes of this forming technique are used in a multitude of industrial applications. Hot rolled special profiles offer innovative solutions whether it be for automotive, materials handling, railroad or thicker flange and web thickness structural steel shapes use. Finished hot rolled steel shapes are roller straightened and sheared into production lengths or sawn into fixed lengths according to customer wishes.

  • Targeted strengthening of highly stressed areas of component parts
  • Best mechanical properties through uninterrupted grain orientation
  • Best shape properties and fitting accuracy by maintenance of the tightest tolerances


Hot Extruding - Extruded Steel Shapes - Steel Extrusions

Hot extruding – Extruded Steel Shapes – Steel Extrusions

During hot extrusion a round steel billet is pre-heated and, after leaving the furnace, is pushed through a forming die into a profile bar using a ram with an extrusion force of 2,200 ton. Hot extrusion offers substantial advantages in comparison to hot rolling forging or machining.
Hot extrusion can be used to make complex profile shapes even using metals which are difficult to form. In addition, small lot sizes can be produced economically.
Hot extruded profiles offer the benefit of:

  • Different material thicknesses within one profile cross-section
  • The possibility to use in highly sensitive areas, where the special profiles must withstand specific demands of temperature, pressure, aggressive media or hygienic requirements
  • Seamless structure of solid and hollow section

Specially Engineered Milled

Specially Engineered Milled (SE-|M|®) Technology

Specially Engineered Milled (SE-|M|®)process for Tight Tolerance and Optimum Hardness for customers whose products require profiles with:

  • 0.2 mm tolerance in the key functional area
  • Harder surface as a result of removal of the decarburised surface layer
  • Cost savings resulting from increased wear resistance

The demands placed on industrial trucks are continuously increasing: they must be faster, higher and more efficient even when subjected to heavy loads. To put it briefly: mast profiles are subjected to extreme loads during use. For a long time, the profile manufacturers were barely able to keep up with the breathtaking pace at which the materials handling industry was developing. Mast profiles, which had remained almost unchanged for decades, forced the industrial truck manufacturers to develop a collection of complex measures to compensate for increased mast lift heights and load pressures. For this reason Hoesch Schwerter Profile GmbH, starting in 2003, carried out research to determine how mast profiles could be designed to achieve greater wear resistance and improved suitability for greater mast lift heights. The result of the years of research: combining the conventional hot rolling process using a suitable material with an efficient machining process makes it possible to meet the highest demands. The ”specially engineered milled process” was patented in 2008.